Best selling sub arcsaw powder welding flux sj101 with good quality

Supplier: Luoyang Refmat Thermal Co., Ltd.
Region: Henan, China
Contact: Mr andy cao
Price: $200.00 /metric ton
Min. Order: 1 metric ton

Click here to contact

Product details

Port:	XINGANG, QINGDAO;	Model Number:	Sj101;
Place of Origin:	Henan China;	Packaging Detail:	JUMBO BAGS;
Delivery Detail:	15 working days;	Payment Terms:	L/C,D/A,D/P,T/T;
Brand Name:	RM;	Supply Ability:	2000 Metric Ton/Metric Tons per Month;

Product Description

Best selling sub arcsaw powder welding flux sj101 with good quality

Standard Conforming: GB/T12470-2003 F48A4-H10Mn2

Equivalent to: AWS A5.23 F7A4-EH14

Description and Applications
SJ101 is a type of fluorine and alkali based agglomerated flux, the basicity of which is about 1.8, gray spherical grains in appearance. Its grain size is 2.0-0.28mm (10-60 meshes). Peony Flux SJ101 is suitable for use with AC or DC power; filler wires connect with Positive Electrode while in DC, the maximum current can reach to 1200 amps. With stable burning arc, the flux provides very good weld bead appearance and excellent slag removal. Additional Feathers are good performance of low temperature impact toughness towards weld bead metals.

CHEMICAL CONTENT SJ101

SiO2+TiO2	CaO+MgO	Al2O3+MnO	CaF2	S	P
20-30	25-35	20-30	15-25	≤0.06	≤0.08

Combined with appropriate SAW wires such as H08MnA, H08MnMoA, H08Mn2MoA, H10Mn2, the flux is capable of welding multiple important low alloy steel structures, like boilers, pressure vessels, and pipelines. Flux SJ101 can also be applied to multi-wire submerged arc welding, especially in double-side single pass welding of large diameter containers.
Mechanical Properties of Deposited Metal

Wire	Tensile Strength	Yield Strength	Elongation	AKV(J)
Wire	R m (MPa)	R eh (MPa)	A %	0℃	-20℃	-40℃
H08MnA	450~550	≥360	≥24	≥110	≥80	≥34
H10Mn2	480~650	≥400	≥24	≥110	≥80	≥34
H08MnMoA	550~650	≥430	≥24	≥70	≥34
H08Mn2MoA	620~750	≥500	≥24	≥70	≥34

Packaging

Unit

bags

Net Weight

25Kg

OPERATION Remarks

1. Redry the flux at 300~350℃ for 2 hours before welding.
2. Impurities such as rust, greasy dirt, moisture, etc. should be cleared from welding area.